SWD696 Series SH106 Two components

 UV resistance polyurethane system

   ship special UV resistance top coating

Descriptions               Since the hull above the waterline exposed to suffer the oceanic atmospheric corrosion and sunshine, common anticorrosion coating is easy to be yellowing, pinking, and even cracking, seriously affect the ship's appearance and application. According to this situation, SWD Urethane Co., USA developed a two components ship special UV-resistance top coating. This coating has high weather resistance performance, without color change, powder and peel off after long term outdoor use and sunshine exposure. It is an ideal ship top coating product which has excellent performance of salt spray resistance and anticorrosion.

Characteristics              Film of coating is colorful, full bright, no powder, no yellowing, anti-aging, with excellent weather resistance and gloss color retention decoration. Coating is dense, with high adhesive strength, wear resistance and tensile resistance, nice physical performances, stable chemical resistance, anticorrosion, wet resistance and salt spray resistance performance. Good compatibility with polyurethane, epoxy, chlorinated rubber, alkyd, phenol-formaldehyde and other paintings, recoating interval is unlimited.

Specifications

Adhesive strength                            11.2Mpa

Impact resistance                             ≥50kg•cm

Temperature variation                         -30------+150℃

Wear resistance（700g/500r）                  10mg

Acid resistance 35%H₂SO₄ or 15%HCI, 30d        no rust no bubbles no peel

Alkali resistance 30%NaOH, 30d                 no rust no bubbles no peel

Salt resistance 100g/L, 30d                       no rust no bubbles no peel

Salt spray resistance 2000h                      no rust no bubbles no peel

Oil resistance 0# diesel Crude oil 30d              no rust no bubbles no peel

Data of performance

Color                        Multiple colors as customers’ need

Luster                        half glazed

Density                       1.05g/cm³ (mixed up)

Volume solid content            81%±2%

VOC                         ≤173g/L

Recommended dry film thickness   50-100μm

Theoretical coverage             0.13kg/sqm (calculated by the above solids percentage and dry film thickness of 100 microns)

Practical coverage                Allow appropriate loss rate

Dry time                       1-3h

Overcoating interval              min: 3h, max: unlimited

Overcoating method              Airless spray, Air spray, Brush, Roller

Flash point                      53℃                   

Recommend procedures

Application scope           Marine industry anticorrosion top coating

Shelf life                  10 months (Indoor with dry and cool conditions)

Packing                    20kg/bucket. 25kg/bucket

Production area             Minhang District, City of Shanghai (15% of raw materials imported  from SWD US）

Security                   To apply this product must be accordance with the relevant national regulation of sanitation, safety and environment. Avoid contacting the wet coating.

Global applicability         Our company aims to provide worldwide customers the same coatings, but sometimes, some small adjustments are made to satisfy each region conditions and international norms, in this case, an alternative product data will be provided.

 Integrity declaration         Our company guarantees the reality of the listed data, due to the diversity and variability of the application environment, please test and verify it before use. We don’t take any other responsibilities except the coating quality self and reserve the right of modification the listed data without prior notice.