SWD952 Series SH109 One component

hand brushable polyurea

    metal structure anticorrosion protective coating

 ­­­

Descriptions                 Over the last decade, spay polyurea elastomer has been widely applied in various filed of model industry for its excellent physical performance and stable chemical media resistance. However, the environment ambient of temperature above 120℃ and strong corrosion conditions will influence the performance of two components polyurea. In order to solve this problem, SWD Urethane Co., USA developed one component hand brushable metal structure anticorrosion protective coating. This coating product can be last long applied in the environment of high temperature 180℃ or 50% sulfuric acid consistence. With high anticorrosion and temperature variation performance, it has been rapidly spread to many heavy duty anticorrosion fields such as petroleum and chemical industry.

Characteristics              The coating is cured by absorption and reaction with air moisture, with high adhesive strength on metal substrate. The presence of large amount of urea bond, biuret bond, urethane bond and hydrogen bond makes it to be excellent in the properties of mechanism and anticorrosion performance, with high performances of acid resistance, alkali resistance, salt resistance, water resistance, temperature variation and chemical resistance. The one component products can be brushed, roller or spray and just open for paint, without special spray equipment.

Specifications

Adhesive strength                            11.5Mpa

Impact resistance                             ≥50kg•cm

Tensile strength                              16Mpa

Elongation                                  360%

Temperature variation                         -40------+180℃

Wear resistance（700g/500r）                  10mg

Acid resistance 50%H₂SO₄ or 15%HCI, 30d        no rust no bubbles no peel

Alkali resistance 50%NaOH, 30d                 no rust no bubbles no peel

Salt resistance 100g/L, 30d                      no rust no bubbles no peel

Salt spray resistance 1000h                      no rust no bubbles no peel

Oil resistance 0# diesel Crude oil 30d              no rust no bubbles no peel

Data of performance

Color                        Multiple colors as customers’ need

Luster                        glazed

Density                       1.03g/cm³

Volume solid content            82%±2%

VOC                         ≤153g/L

Recommended dry film thickness   100-200μm

Theoretical coverage             0.13kg/sqm (calculated by the above solids percentage and dry film thickness of 100 microns)

Practical coverage                Allow appropriate loss rate

Dry time                       1-3h

Overcoating interval              min: 3h, max: 28h

Overcoating method              Airless spray, Air spray, Brush, Roller

Flash point                      59℃

 Recommend procedures                        

Application scopes         Petroleum, chemical industry, transportation, building, electrical and other industries.

Shelf life                  10 months (Indoor with dry and cool conditions)

Packing                    20kg/bucket. 25kg/bucket

Production area            Minhang District, City of Shanghai (28% of raw materials imported from SWD US)

Security                   To apply this product must be accordance with the relevant national regulation of sanitation, safety and environment. Avoid contacting the wet coating.

Global applicability         Our company aims to provide worldwide customers the same coatings, but sometimes, some small adjustments are made to satisfy each region conditions and international norms, in this case, an alternative product data will be provided.

Integrity declaration         Our company guarantees the reality of the listed data, due to the diversity and variability of the application environment, please test and verify it before use. We don’t take any other responsibilities except the coating quality self and reserve the right of modification the listed data without prior notice.